Specifications
|
|
Material:
|
Laminated impact Acrylic |
|
Finish:
|
Brushed |
|
Sheet Size:
|
24" x 48¾" - Full
24" x 24" - Half
12" x 24" - Quarter |
|
Thickness 1-Ply:
|
NONE |
|
Thickness 2-Ply:
|
1/16" (1.6mm)
1/8" (3.2mm) |
|
Thickness 3-Ply:
|
NONE |
|
Usage:
|
Interior signage
Exterior signage
Personal Identification |
|
Engraving Method:
|
Rotating Carbide
|
|
Cutting Depth:
|
.012" (.30mm) |
|
Capabilities
|
|
Scores
|
|
|
Bonds
|
|
Saws
|
|
|
Permits Fine Engraving
|
|
Drills
|
|
|
UV Stable
|
|
Shears
|
|
|
Back-Filling
|
|
Laser Vector Cuts
|
|
|
Back-Lighting
|
|
Bevels
|
|
|
Braille-Engravable
|
|
Heat Bendable
|
|
|
Embosses
|
|
Screen Prints
|
|
|
Ink Prints
|
|
Hot Stamps
|
|
|
Thermal Prints
|
MSDS
information |
|
Physical Properties
|
Typical Values |
ASTM Method |
| IZOD Impact Strength
|
| Notched at 73°F (22.777°C) |
1.2 ft lbs/in |
D-256 |
| Notched at 32°F (0°C) |
.7 ft lbs/in |
D-256 |
| Tensile Strength |
| To break |
5,400 psi |
D-638 |
| Elongation before break |
35% |
D-638 |
| Flexural Strength |
| Loan to stretch outer surface 5% |
7,000 psi |
D-790 |
| Specific Gravity |
1.15 |
D-792 |
| Rockwell Hardness |
R99, L77 |
D-785 |
| Deflection Temperature |
| Temperature at which material deflects .010"
(.254mm) at 264 psi |
170°F (76.66°C) |
D-648 |
| Coefficient of Thermal
Expansion |
| Inch/inch/°F |
3.8 x 10-5 |
D-696 |
|
| OUTDOOR METALS engraving material softens at about
200°F (93.33°C) sufficiently so that it can be bent as needed. It
can be sawed, drilled and bonded, but not sheared. For best
appearance, sawed edges should be buffed on material 1/8" (3.0mm)
and thicker. |
| The base and cap materials, as well as the foils, were tested
for flammability by Underwriters Laboratories. The base and cap
materials are rated 94 HB on the UL 94 test. The foil was judged
as not contributing to the combustion of the base material. |
| Prolonged tests in the laboratory to evaluate fading resulted
in no noticeable change in colors after 500 hours of
exposure in the Fade-O-Meter tester. |
|
|