Specifications
|
|
Material:
|
Acrylic Cap, ABS Core |
|
Finish:
|
Brushed |
|
Sheet Size:
|
24" x 48¾" - Full
24" x 24" - Half
12" x 24" - Quarter |
|
Thickness 1-Ply:
|
NONE |
|
Thickness 2-Ply:
|
1/32" (.8mm)
Use 112 as first three digits in item code
1/16" (1.6mm)
Use 122 as first three digits in item code
3/32" (3.2mm)
Use 132 as first three digits in item code |
|
Thickness 3-Ply:
|
NONE |
|
Usage:
|
Interior signage
Personal Identification |
|
Engraving Method:
|
Rotating Carbide
|
|
Cutting Depth:
|
.012" (.30mm) |
|
Capabilities
|
|
Scores
|
|
|
Bonds
|
|
Saws
|
|
|
Permits Fine Engraving
|
|
Drills
|
|
|
UV Stable
|
|
Shears
|
|
|
Back-Filling
|
|
Laser Vector Cuts
|
|
|
Back-Lighting
|
|
Bevels
|
|
|
Braille-Engravable
|
|
Heat Bendable
|
|
|
Embosses
|
|
Screen Prints
|
|
|
Ink Prints
|
|
Hot Stamps
|
|
|
Thermal Prints
|
MSDS
information |
|
Physical Properties
|
Typical Values |
ASTM Method |
| IZOD Impact Strength
|
| Notched at 73°F (22.777°C) |
2 ft lbs/in |
D-256 |
| Notched at 32°F (0°C) |
1.6 ft lbs/in |
D-256 |
| Notched at 0°F (<17.76>°C) |
1.2 ft lbs/in |
D-256 |
| Unnotched at 73°F (22.755°C) |
24 ft lbs/in |
D-256 |
| Tensile Strength |
| To break |
7,000 psi |
D-638 |
| Elongation before break |
29% |
D-638 |
| Flexural Strength |
| Loan to stretch outer surface 5% |
11,000 psi |
D-790 |
| Specific Gravity |
1.11 |
D-792 |
| Rockwell Hardness |
R114, M45 |
D-785 |
| Deflection Temperature |
| Temperature at which material deflects .010"
(.254mm) at 264 psi |
186°F (85.55°C) |
D-648 |
| Coefficient of Thermal Expansion |
| Inch/inch/°F |
5.0 x 10-5 |
D-696 |
|
| The plastic material used in the manufacture of the VALUE
SERIES SATINS was specifically selected and formulated to achieve
the best balance of properties needed for the engraving industry. |
| The material softens sufficiently at about 200°F, which enables
bending, should that be desired. It can also be drilled, sawed,
sheared, nailed and bonded to itself or other materials. |
| Most of the colors will exhibit slight fading under prolonged
exposure to direct sunlight. There are, however, those which tend to
fade more severely. This material is designed for use where no direct
extreme exposure is encountered. |
| The base and cap material were tested for flammability by
Underwriters Laboratories. They are rated at 94HB on the UL 94 test.
|
|